poly and tension questions

Discussion in 'Strings' started by tomato123, Oct 1, 2004.

  1. tomato123

    tomato123 New User

    Joined:
    Aug 2, 2004
    Messages:
    55
    Just some thoughts and questions following my first time using poly strings is:

    I had it strung a Lux. Ace at 10% lower tension as Luxilion recommended, but I don't know if that necessarily meant that stringing it at 54lbs translates into a 60lb. feel, but it certainly did not feel like 60lbs (it felt a lot looser) and thus I had to take some power off my swing and adjust to the power that the string provided. Is that because poly provides more power than a regular synth gut, or is it because of the tension indeed is 54lbs and not 60, or both? Also, after playing with it for about a good 2 weeks or so, it felt even more "wabbly" which I presume is because of the tension loss, so to those who regularly use poly strings, do you usually end up cutting them yourself before they break on their own? Since it seems like they don't break very easily, I would figure that it also has that much more room to deteriorate in playability. So I'd like to get some feedback regarding those two questions. Thanks.
     
    #1
  2. LoveThisGame

    LoveThisGame Professional

    Joined:
    Feb 18, 2004
    Messages:
    1,016
    From reading this forum, I am definitely in the minority because I don't drop tension on polys.

    1) They lose tension more readily than most other strings.

    2) Personally, I prefer stiffer, crisper strings. (When I test multifilaments, I have to force myself not to cut them out after one day and find myself using them for only one set at most.)

    3) I have had no problems or complaints from customers.

    I do have a strong preference for poly hybrids, both from the customer's viewpoint and stringing.
     
    #2
  3. pure luck

    pure luck New User

    Joined:
    Sep 11, 2004
    Messages:
    27
    indeed u have to drop tension on poly strings but only 2lbs

    poly strings normally do not snap

    enjoy your play :)
     
    #3
  4. Marc C.

    Marc C. Rookie

    Joined:
    Feb 19, 2004
    Messages:
    252
    Stringing polys in the crosses is a *****.
     
    #4
  5. David Pavlich

    David Pavlich Professional

    Joined:
    Feb 11, 2004
    Messages:
    1,203
    The reason for dropping tension is because polys are much stiffer than the usual synthetic. 60 lbs reference tension is 60 lbs reference tension, regardless of the string type. However, strings like Kevlar or poly have much less elongation percentages relative to synthetics and gut.

    You lower the tension to reduce stringbed stiffness. You have to experiment with reference tension in order to match what you used to play with.

    Also, polys are notorious for high initial tension loss so keep this in mind when determining what is good for you.

    David
     
    #5