Quote:
Originally Posted by Rabbit
^^^^^
I think what's more the case is the resins bonding the graphite break down, not the graphite. This causes the frame to become more flexible. I have seen this with my older C10s.
|
I doubt the carbon fibers themselves are damaged by stress. But, you think the carbon fiber reinforced resin is suffering stress fractures? Or are you talking about a chemical reaction breakdown?