If you are breaking your poly mains, 16g will give more durability and less spin unless you go to a shaped/textured string.
If they are dying quickly, gauge won't make much difference.
Some polys, like SPPP, just have better tension maintenace.
If you are leaving the poly in long enough to break the crosses, maybe you don't need to be using a poly/syn hybrid at all.
Which strings, specifically, are you using and how many hours do you expect them to last?