I've had a reel of volkl v-torque tour 1.25mm that I've never really gelled with. It's a co-poly.
Always great for like 20-30 minutes before massive tension loss and soon has way too much pop, even strung in 60s.
My thoughts are to ask stringer to do maximum prestretch (20%) with longest possible pulls, to stretch it as much as possible. Going to try it at 57/53. I've never tried it prestretched but from all I've been reading, it seems like an excellent candidate to actually transform it into a much better actually usable string, by taming its crazy pop.
My question is... would anyone have an estimate of how much longer this will could make the string (if by much at all)?
Just curious if max prestretch would actually thin the string out so it's actually closer to 1.20mm. cause that would actually be pretty cool haha.
Going to try it in a beefed up vcore 95 2021
Always great for like 20-30 minutes before massive tension loss and soon has way too much pop, even strung in 60s.
My thoughts are to ask stringer to do maximum prestretch (20%) with longest possible pulls, to stretch it as much as possible. Going to try it at 57/53. I've never tried it prestretched but from all I've been reading, it seems like an excellent candidate to actually transform it into a much better actually usable string, by taming its crazy pop.
My question is... would anyone have an estimate of how much longer this will could make the string (if by much at all)?
Just curious if max prestretch would actually thin the string out so it's actually closer to 1.20mm. cause that would actually be pretty cool haha.
Going to try it in a beefed up vcore 95 2021